the reason:
(1) The difference in the warp and weft direction causes the substrate size to change; due to the shearing, the fiber direction is not noticed, so that the shear stress remains in the substrate, and once released, it directly affects the shrinkage of the substrate size.
(2) The copper foil portion of the substrate surface is etched away from the variation of the substrate, and a dimensional change occurs when the stress is removed.
(3) When the plate is brushed, the pressure is too large, causing the tensile stress to cause deformation of the substrate.
(4) The resin in the substrate is not completely cured, resulting in dimensional change.
(5) In particular, before the lamination of the multilayer board, the storage conditions are poor, and the thin substrate or the prepreg is hygroscopic, resulting in poor dimensional stability.
(6) When the multilayer board is pressed, excessive flow of glue causes deformation of the glass cloth.
Solution:
(1) Determine the variation law of the warp and weft direction to compensate on the film according to the shrinkage rate (this work is performed before the light painting). At the same time, it is processed in the fiber direction when cutting, or processed according to the character mark provided by the manufacturer on the substrate (generally, the vertical direction of the character is the longitudinal direction of the substrate).
(2) When designing the circuit, the entire board surface should be distributed as evenly as possible. If it is not possible, you must also leave a transition in the space (does not affect the circuit position). This is due to the difference in the warp and weft strength of the sheet due to the difference in the warp and weft yarn density in the glass cloth structure.
(3) The test brush should be used to make the process parameters in the best condition, and then the rigid plate is carried out. For thin substrates, chemical cleaning or electrolytic processes should be used for cleaning.
(4) Take the baking method to solve. In particular, baking is performed before drilling, and the temperature is 120 ° C for 4 hours to ensure the curing of the resin, and to reduce the deformation of the substrate due to the influence of heat and cold.
(5) The inner layer of the oxidized substrate must be baked to remove moisture. The treated substrate is stored in a vacuum drying oven to prevent moisture absorption.
(6) Process pressure test is required, and the process parameters are adjusted and then pressed. At the same time, according to the characteristics of the prepreg, the appropriate amount of glue can be selected.
Open Frame For Capacitive Touch Monitor
The open frame touchscreen monitor is a product developed and designed by ourselves. It has been sold for more than 6 years and has exceeded 160,000 units. At present, it is running very well. It mainly customizes different touch technologies, different sizes, different interfaces, connecting cables and power supply parts to meet the needs of guests. Our open frame capacitive touchscreen monitor used of PCAP 10 points touch technology, and customize various interfaces for customers, such as: VGA, DVI, HDMI, DP and so on. It is mainly used in banks, hospitals, government units, airports, railway stations, supermarkets, real estate and other places.
Open frame Touchscreen monitor(2C series) Product developed by GreenTouch
Size support: 15inch~ 55inches,
Touch technology: Capacitive Touch Screen technology, supports 10-point touch.
Surface support: explosion-proof IK08, dustproof and waterproof IP65.
Standard VESA: 75mm * 75mm and 100mm * 100mm
Input interface: VGA. DVI.HDMI, DP.Mic.Audio out and other combinations.
Input power: DC12V / 4A or AC80-240V,
Product certificate: support CE, FCC, CB, UL ,HDMI certification optionsS
Pruduct Show:
Open Frame Capacitive Touch Monitor,PCAP Touch Screen Monitor,IP65 Touch Monitor,Portable Touch Screen Monitor,Projected Capacitive Touch Screen Monitor,Touch Screen Display Monitor
ShenZhen GreenTouch Technology Co.,Ltd , https://www.bbstouch.com